Complete list of products:
Nitrading
Carburizing
| MONOSSAL System: |
| Products |
Working Temperature |
Characteristics |
| CC 50 |
850-950ºC |
Offers a smooth carbon gradient, also used in carbon restauration |
| CC 80 |
850-950ºC |
Indicated for the carburizing of alloyed steels |
| CC 110 |
850-950ºC |
Indicated for the carburizing of non-alloyed steels, where great depth is demanded |
| C 85 |
850-950ºC |
Same application of CC80, indicated when there is great salt drag out caused by the treated parts |
| C 97 |
850-950ºC |
Same application of CC110, indicated when there is little salt drag out caused by the treated parts |
| C 4 |
780-950ºC |
Extremely fluid salt for layers up to 0,8 mm |
| 2 SALTS system: |
| Products |
Working Temperature |
Characteristics |
| A 5 / C3B |
850-1000ºC |
Bath activated for layers up to 2,0 mm |
| C 5 / C3B |
850-1000ºC |
Bath extremely activated for layers up to 2,5 mm |
| GS540/C3B (10%) |
850-950ºC |
Bath weakly activated for layers up to 0,6 mm |
| GS580/C3B (10%) |
850-950ºC |
Bath weakly activated for layers up to 0,3 mm |
| Solid carburizing – granulates for pack carburizing |
| Products |
Working Temperature |
Characteristics |
| KG 6 |
900-950ºC |
Recommended for most applications |
| KG 30 |
900-950ºC |
Recommended when an activer carburizing medium is necessary |
Carbonitriding
Hardening and annealing
| Hardening of HIGH SPEED STEELS |
| Products |
Working Temperature |
Characteristics |
| SN 1100 |
1100-1300ºC |
Completely prevent decarburization |
| SN 1080 |
1080-1300ºC |
| SN 950 |
1000-1300ºC |
| CN |
1050-1300ºC |
Neutral heating bath. It can also be used for the treating of hot work tool steels |
| Heat treatment of HIGH ALLOYED STEELS |
| Products |
Working Temperature |
Characteristics |
| GS 750 / R2 |
900-1100ºC |
Neutral bath. Completely prevents decarburization |
| GS 540 / SN 950 |
950-1100ºC |
Totally neutral. Recommended for extremely sensitive parts |
| HEATING BATHS WITH CYANIDE (when a small carbon enrichment is not damaging) |
| Products |
Working Temperature |
Characteristics |
| GS540/C3B (5%) |
600-950ºC |
Indicated for hardening of steels with aproximately 1% carbon |
| GS580/C3B (5%) |
580-950ºC |
Used with medium carbon level steels |
| GS660/C3B (10%) |
580-950ºC |
| GSL |
750-840ºC |
Single-salt bath, developed especially for the treatment of files |
| NEUTRAL HEATING baths (recommended when no kind of reaction is allowed on the metal surface) |
| Products |
Working Temperature |
Characteristics |
| GS 540 / R2 |
600-950ºC |
Heat treatment of steels in general and pre-heating of high speed steels |
| GS 660 / R3 |
700-900ºC |
Heat treatment of steels in general, especially when followed by oil quenching |
| GS 580 / R1 |
680-920ºC |
For generic applications, especially on parts less sensible to decarburization |
| Coarse grain ANNEALING |
| Products |
Working Temperature |
Characteristics |
| GS 960 |
1000-1200ºC |
Indicated to facilitate the machinability of the parts, as well as for the saturation of new ceramic linings |
Quenching and tempering
| MARTEMPERING, AUSTEMPERING AND TEMPERING |
| Products |
Working Temperatute |
Characteristics |
| AS 300 |
330-550ºC |
AS salt to be used is chosen based on the lowest working temperature |
| AS 270 |
300-550ºC |
| AS 235 |
260-550ºC |
| AS 220 |
250-550ºC |
| AS 170 |
190-550ºC |
| AS 140 |
160-550ºC |
| QUENCHING AND TEMPERING |
| Products |
Working Temperatute |
Characteristics |
| GS 430 / GS 520 |
500-700ºC |
Indicated for quenching and tempering of high speed steels and high alloyed steels |
| GS 230 |
270-600ºC |
Indicated for quenching and tempering of steels in general |
Quenching water aditives
| Products |
Working Temperature |
Characteristics |
| AWS 20 |
< 60ºC |
Provide quenching uniformity by eliminating vapor bubbles (SN: no nitrite) |
| AWS 33 (SN) |
< 60ºC |
Cleaning of metallic surfaces
| Products |
Working Temperature |
Characteristics |
| KLN DeNamel |
450-600ºC |
Removal of porcelain enamels and residues of cast sand based on zirconite and alumina |
| KLN DGS |
370-540ºC |
Removal of scales in heatresistant stainless steels, titanium and its alloys |
| KLN 4 |
500-620ºC |
Removal of cast sand and removal of free graphite in cast irons |
| KLN 5 |
370-600ºC |
Removal of paint on fixtures, grids and grills |
| KLN 6 |
300-600ºC |
Removal of organic residues in general |
| KLN 10 |
300-600ºC |
Removal of synthetic fibers, rubber and other organic substances |
Heat transfer and vulcanization
| Products |
Working Temperature |
Characteristics |
| Effge ASD |
180-600ºC |
Used in chemical industries as thermal fluid for heat transfer |
| Rubbercure |
160-260ºC |
Used for rubber vulcanization |
Nonferrous metals heat treatment
| Products |
Working Temperature |
Characteristics |
| GS 750 / R2 |
900-1100ºC |
Annealing of titanium, zirconium, tungsten, molybdenum and its alloys |
| GS 540 / R2 |
600-950ºC |
| GS 560 |
600-850ºC |
Annealing of silver, gold and its alloys |
| GS 560 / C2 |
580-850ºC |
| GS 560 / C2 (C3B) |
580-700ºC |
Annealing of brass, copper and nickel-silver alloys |
| GS 660 / C2 (C3B) |
600-700ºC |
| AS 300 |
330-550ºC |
This salt can be exceptionaly used for the annealing of the MS 63 brass |
| AVS 250 |
300-550ºC |
Solubilization of aluminium alloys, containing maximum 10% magnesium |
Blackening
| Products |
Working Temperature |
Characteristics |
| Ferroblack 1 |
135-140ºC |
HOT blackening. Produces an uniform and adherent blackening on the metallic surfaces of mild and alloyed steels (with crhome leves under 12%) |
| Ferroblack 2 |
135-140ºC |
| Blackfast 181 |
20-30ºC |
ROOM TEMPERATURE BLACKENING solution for steel and cast iron |
| Blackfast 551 |
20-30ºC |
Conditioning solution for ROOM TEMPERATURE BLACKENING |
| Blackfast 716B |
20-80ºC |
Alkaline degreaser used in the ROOM TEMPERATURE BLACKENING process |
| Blackfast 833B |
20-30ºC |
Dewatering and proctetive oil used in the ROOM TEMPERATURE BLACKENING process |
Brazing pastes
| Products |
Working Temperature |
Characteristics |
| Pasta de cobre |
1100ºC |
Used in brazing processes of MILD STEEL parts, within furnaces with controlled atmosphere |
| Pasta de cobre ESPECIAL |
1100ºC |
Used in brazing processes of STAINLESS STEEL parts, within furnaces with controlled atmosphere |
| Pasta de bronze |
1050ºC |
Used in brazing processes of MILD STEEL parts, within furnaces with controlled atmosphere |
| Pasta de bronze ESPECIAL |
1050ºC |
Used in brazing processes of STAINLESS STEEL parts, within furnaces with controlled atmosphere |
Nickel catalysts
| Products |
Working Temperature |
Characteristics |
| Catalisador A5 |
1000ºC |
Used in ENDOTHERMIC GAS GENERATORS |
| Catalisador A8 |
950ºC |
Used in AMMONIA dissociators and endothermic gas generators based on ethyl alcohol. |
|